PENGGUNAAN HIGH RESOLUTION NEUTRON POWDER DIFFRACTOMETER UNTUK MENENTUKAN STRUKTUR KRISTAL DAN MAGNETIK SENYAWA La0,47Ca0,53Mn1-yCuyO3 (0 y 0,09) - Hallo sahabat Sheva Permana Blog, Pada Artikel yang anda baca kali ini dengan judul PENGGUNAAN HIGH RESOLUTION NEUTRON POWDER DIFFRACTOMETER UNTUK MENENTUKAN STRUKTUR KRISTAL DAN MAGNETIK SENYAWA La0,47Ca0,53Mn1-yCuyO3 (0 y 0,09), kami telah mempersiapkan artikel ini dengan baik untuk anda baca dan ambil informasi didalamnya. mudah-mudahan isi postingan Artikel Jurnal, Artikel Jurnal Sains Indonesia, yang kami tulis ini dapat anda pahami. baiklah, selamat membaca.

Judul : PENGGUNAAN HIGH RESOLUTION NEUTRON POWDER DIFFRACTOMETER UNTUK MENENTUKAN STRUKTUR KRISTAL DAN MAGNETIK SENYAWA La0,47Ca0,53Mn1-yCuyO3 (0 y 0,09)
link : PENGGUNAAN HIGH RESOLUTION NEUTRON POWDER DIFFRACTOMETER UNTUK MENENTUKAN STRUKTUR KRISTAL DAN MAGNETIK SENYAWA La0,47Ca0,53Mn1-yCuyO3 (0 y 0,09)

PENGGUNAAN HIGH RESOLUTION NEUTRON POWDER DIFFRACTOMETER UNTUK MENENTUKAN STRUKTUR KRISTAL DAN MAGNETIK SENYAWA La0,47Ca0,53Mn1-yCuyO3 (0 y 0,09)

ABSTRAK

PENGGUNAAN HIGH RESOLUTION NEUTRON POWDER DIFFRACTOMETER UNTUK

MENENTUKAN STRUKTUR KRISTAL DAN MAGNETIK SENYAWA 

La0,47Ca0,53Mn1-yCuyO3 (0 < y < 0,09). Telah dianalisis pada suhu ruang dan suhu rendah struktur kristal dan magnetik sampel La0,47Ca0,53Mn1-yCuyO3 0 < y < 0,09 menggunakan High Resolution Neutron Powder Diffractometer (HRPD). Didapatkan bahwa pada suhu ruang dan suhu rendah, sampel mempunyai struktur kristal orthorhombic dengan space group Pnma. Semakin meningkat nilai x, maka volume kisi semakin besar juga. Pada suhu ruang sampel mempunyai sifat paramagnetik, sedangkan pada suhu rendah bersifat antiferomagnetik bercampur feromagnetik. Nilaimomen magnetik semakin kecil seiringmeningkatnya nilai x.

Kata kunci : Struktur kristal dan magnetik, High Resolution Powder Diffraction

ABSTRACT

DETERMINATION OFCRYSTALANDMAGNETIC STRUCTURE 

OFLa0.47Ca0.53Mn1-yCuyO3

(0 < y < 0.09) USING HIGH RESOLUTION NEUTRON POWDER DIFFRACTOMETER. 

Crystal and magnetic structure of La0.47Ca0.53Mn1-yCuyO3 with 0 < y < 0.09 at low and room temperature have been analyzes using High Resolution Neutron Powder Diffraction (HRPD). It is obtained that at room temperature as well as at low temperature, the samples have orthorhombic structure with Pnma space group. Increasing x value, will increase the lattice volume. At room temperature, samples have paramagnetic stucture, while at low temperature have antiferromagnetic structure. The value of magnetic moment will decrease with increasing x value.

Keywords: Crystal and magnetic structure, High Resolution Powder Diffraction

DOWNLOAD

Demikianlah Artikel PENGGUNAAN HIGH RESOLUTION NEUTRON POWDER DIFFRACTOMETER UNTUK MENENTUKAN STRUKTUR KRISTAL DAN MAGNETIK SENYAWA La0,47Ca0,53Mn1-yCuyO3 (0 y 0,09)

Sekianlah artikel PENGGUNAAN HIGH RESOLUTION NEUTRON POWDER DIFFRACTOMETER UNTUK MENENTUKAN STRUKTUR KRISTAL DAN MAGNETIK SENYAWA La0,47Ca0,53Mn1-yCuyO3 (0 y 0,09) kali ini, mudah-mudahan bisa memberi manfaat untuk anda semua. baiklah, sampai jumpa di postingan artikel lainnya.

Anda sekarang membaca artikel PENGGUNAAN HIGH RESOLUTION NEUTRON POWDER DIFFRACTOMETER UNTUK MENENTUKAN STRUKTUR KRISTAL DAN MAGNETIK SENYAWA La0,47Ca0,53Mn1-yCuyO3 (0 y 0,09) dengan alamat link https://shevapermanas.blogspot.com/2016/10/PENGGUNAAN-HIGH-RESOLUTION-NEUTRON-POWDER-DIFFRACTOMETER.html

Tweet

Subscribe to receive free email updates: