MODIFIKASI SINTESIS DAN PENINGKATAN KARAKTERISTIK MAGNETIK NANOPARTIKEL CORE/SHELL Fe/Oksida Fe HASIL REAKSI REDUKSI BOROHIDRIDA - Hallo sahabat Sheva Permana Blog, Pada Artikel yang anda baca kali ini dengan judul MODIFIKASI SINTESIS DAN PENINGKATAN KARAKTERISTIK MAGNETIK NANOPARTIKEL CORE/SHELL Fe/Oksida Fe HASIL REAKSI REDUKSI BOROHIDRIDA, kami telah mempersiapkan artikel ini dengan baik untuk anda baca dan ambil informasi didalamnya. mudah-mudahan isi postingan Artikel Jurnal, Artikel Jurnal Sains Indonesia, yang kami tulis ini dapat anda pahami. baiklah, selamat membaca.

Judul : MODIFIKASI SINTESIS DAN PENINGKATAN KARAKTERISTIK MAGNETIK NANOPARTIKEL CORE/SHELL Fe/Oksida Fe HASIL REAKSI REDUKSI BOROHIDRIDA
link : MODIFIKASI SINTESIS DAN PENINGKATAN KARAKTERISTIK MAGNETIK NANOPARTIKEL CORE/SHELL Fe/Oksida Fe HASIL REAKSI REDUKSI BOROHIDRIDA

MODIFIKASI SINTESIS DAN PENINGKATAN KARAKTERISTIK MAGNETIK NANOPARTIKEL CORE/SHELL Fe/Oksida Fe HASIL REAKSI REDUKSI BOROHIDRIDA

ABSTRAK

MODIFIKASI SINTESIS DAN PENINGKATAN KARAKTERISTIK MAGNETIK

NANOPARTIKELCORE/SHELLFe/Oksida FeHASILREAKSIREDUKSIBOROHIDRIDA.

Telah dibuat nanopartikel berstruktur core/shell Fe/oksida Fe dengan nilai magnetisasi tinggi melalui tahapan reaksi reduksi FeCl3 oleh reduktor Natrium Borohidrida (NaBH4), pencucian endapan dalam etanol, pemanasan 75 oC dalam suasana vakum, dilanjutkan dengan proses oksidasi terkendali
dengan pereaksi Trimethylamine N-Oxide (TMNO). Morfologi struktur nanopartikel core/shell dipelajari dari foto hasil pengamatan dengan Transmission Electron Microscope (TEM), sifat magnetik ditentukan dari kurva histeresis hasil pengukuran dengan Vibrating Sample Magnetometer (VSM) dan fasa dianalisis dari pola difraksi sinar-X. Diperoleh bahwa karakteristik magnetik yang terbentuk dipengaruhi oleh kondisi proses pencucian untuk menghilangkan fasa sisa reaktan dan kondisi pemanasan untuk penyempurnaan reaksi pembentukan core. Pemanasan yang terlalu lama cenderung menurunkan sifat magnetik karena meningkatkan fasa-fasa minor FeB dan Fe2B. Pada tahapan oksidasi, selain pembentukan lapisan shell oksida Fe pada permukaan core Fe, juga terjadi proses reduksi fasa minor tersebut dan memberikan peningkatan sifat magnetik. Karakteristik optimal nanopartikel dengan ukuran kristalin ~ 8 nmdalampartikel core Fe berukuran < 30 nmdan shell oksida Fe setebal ~ 3 nm dengan magnetisasi saturasi Ms ~ 130 emu/gram diperoleh pada proses sintesis dengan pencucian 15x diikuti pemanasan 4 jam.

Kata kunci: Magnetik nanopartikel, Core-shell, Fe/Oksida Fe, Reduksi

ABSTRACT

SYNTHESIZE MODIFICATION AND MAGNETIC CHARACTERISTIC IMPROVEMENT

OF Fe/Fe OXIDE CORE/SHELL NANOPARTCLE PRODUCE BY BOROHYDRYDE REDUCTION REACTION. 

Nanoparticle of Fe/Fe oxide core/shell structure with high magnetization values has been successfully sinthesized through reduction of FeCl3 by NaBH4 reductor, repeat washing in ethanol, heat treatment at 75 oC and vacuum atmosphere, followed by controlled oxidation with Trimethylamine N-Oxide (TMNO). Morphological structure of the core/shell nanoparticles were evaluated from the image observed with Transmission Electron Microscope (TEM), magnetic properties through the hysteresis curve measured byVibrating SampleMagnetometer (VSM) while the phase were analysed fromits X-Ray diffraction patterns. Magnetic characteristics of the nanoparticles are found to be affected by the condition of washing process to remove residual phase reactants and heat treatment conditions for the completion of core formation. Too long heating tend to lowered the magnetic properties due to increasing of FeB and Fe2B minor phases. During oxidation process, beside formation of Fe oxide shell on the surface of Fe core, reduction of these minor phases was also proceed and resulted in enhanced ofmagnetic properties. Optimal characteristics of nanoparticle with a crystalline size of ~ 8 nm within Fe core of < 30 nm particle size and Fe oxide shell of ~ 3 nm thickness with saturation magnetization Ms ~ 130 emu/g obtained in the synthesis with 15x washing steps followed by heat treatment at 4 hours.

Keywords:Magnetic nanoparticle, Core-shell, Fe/Oksida Fe, Reduction

DOWNLOAD

Demikianlah Artikel MODIFIKASI SINTESIS DAN PENINGKATAN KARAKTERISTIK MAGNETIK NANOPARTIKEL CORE/SHELL Fe/Oksida Fe HASIL REAKSI REDUKSI BOROHIDRIDA

Sekianlah artikel MODIFIKASI SINTESIS DAN PENINGKATAN KARAKTERISTIK MAGNETIK NANOPARTIKEL CORE/SHELL Fe/Oksida Fe HASIL REAKSI REDUKSI BOROHIDRIDA kali ini, mudah-mudahan bisa memberi manfaat untuk anda semua. baiklah, sampai jumpa di postingan artikel lainnya.

Anda sekarang membaca artikel MODIFIKASI SINTESIS DAN PENINGKATAN KARAKTERISTIK MAGNETIK NANOPARTIKEL CORE/SHELL Fe/Oksida Fe HASIL REAKSI REDUKSI BOROHIDRIDA dengan alamat link https://shevapermanas.blogspot.com/2016/10/MODIFIKASI-SINTESIS-DAN-PENINGKATAN-KARAKTERISTIK-MAGNETIK.html

Tweet

Subscribe to receive free email updates: